| Summary/Abstract |
Heusler type alloys Ni50Mn25+xGa25-x (x=2,3,4 and 5) based on near stoichiometric Ni2MnGa compositions were directionally solidified using modified Bridgman method. The alloys thus prepared were characterized for their chemical composition, crystal structure, microstructure, phase transformation, magnetic and magneto-mechanical properties. The directionally solidified Ni50Mn30Ga20 alloy rod exhibited maximum magnetocrystalline value of 95 kJm-3 and lowest detwinning stresses for martensite phase of about 5MPa. The reversible room temperature magnetic field induced strain of 0.2% under external magnetic field of 0.6T and 0.05kN bias load was obtained for the directionally solidified Ni50Mn30Ga20 alloy.
|